Characterisation of APS TBC system during isothermal oxidation at 1100°C
Silesian University of Technology WSK “PZL Rzeszów”
2009/12/1
Purpose: The purpose of presented investigations was metallographical characterization of failure modes of air
plasma sprayed thermal barrier coatings system in isothermal oxidation test conditions a...
Characterisation of air plasma sprayed TBC coating during isothermal oxidation at 1100°C
Thin & thick coatings TBC Degradation Oxidation
2010/2/22
Purpose: The purpose of the research was characterization of failure modes of air plasma sprayed thermal barrier coatings system in isthermal oxidation test conditions at 1100ºC.
Design/methodol...