钨改性TiO2可见光下去除水中阿替洛尔的性能
钨改性 TiO2 可见光催化 阿替洛尔
2019/3/12
提高自然条件下水中阿替洛尔的光催化降解速率，降低阿替洛尔对环境的影响，以钛酸正丁酯为Ti源，偏钨酸铵为W源，采用溶胶-凝胶法制备掺钨TiO2，通过X线衍射(XRD)、紫外可见漫反射光谱(UV-vis)、比表面积分析(BET)和扫描电子显微镜(SEM)等方法考察掺钨量(物质的量比)、煅烧温度、催化剂及底物初始质量浓度对阿替洛尔降解率的影响，同时对光催化氧化阿替洛尔的反应机理进行研究。研究结果表明：在...
Complete Oxidation of Benzene over Au-V2O5/TiO2 and Au-V2O5/ZrO2 Catalysts
Complete Oxidation Benzene Au-V2O5/TiO2
2009/7/29
A gold promotional effect is reported for the complete oxidation of benzene using Au/V2O5 supported on titania or zirconia catalysts.
Photocatalytic Methanol Reforming on Au/TiO2 for Hydrogen Production
Photocatalytic Reforming Au/TiO2
2009/7/28
Methanol can be reformed with water, at ambient
temperature, using photocatalysis, and this reaction
represents a possible low energy, more sustainable
pathway to hydrogen production than (for inst...
Preparation of a Monolith-Supported Au/TiO2 Catalyst Active for CO Oxidation
cordierite monolith gold on titania CO oxidation
2009/7/28
The development of a method for making an
adherent coating of Au/TiO2 on a cordierite monolith
is described. The optimum method entails first
forming a wash-coat of TiO2 by combining a colloidal
d...
A Novel Internally Heated Au/TiO2 Carbon-Carbon Composite Structured Reactor for Low- mperature CO Oxidation
Au/TiO2 Carbon-Carbon
2009/7/28
A compact, internally heated, catalytic reactor is
demonstrated for the low-temperature oxidation of
carbon monoxide. Carbon nanofibres were grown
on carbon felt and used as a support material for
...
Effects of Au Nanoparticles on TiO2 in the Photocatalytic Degradation of an Azo Dye
Au Nanoparticles Photocatalytic Degradation
2009/7/28
The photocatalytic activity of Au modified titanium
dioxide was evaluated in the photodegradation of
the azo dye Acid Red 1 (AR1) under 254 nm
irradiation. Noble metal nanoparticles were
deposited...
Properties of TiO2 Support and the Performance of Au/TiO2 Catalyst for CO Oxidation Reaction
gold titanium dioxide carbon monoxide oxidation
2009/7/28
Gold catalysts were prepared on TiO2 supports of
different phase structures (i.e., anatase, rutile and
biphasic), TiO2 crystal size (i.e., 9-23 nm), surface
and textural properties (i.e., hydration...
An unconventional Au/TiO2 PROX system for complete removal of CO from non-reformate hydrogen
Au/TiO2 PROX system CO non-reformate hydrogen
2009/7/28
Au-based catalysts, generally known for high activity
in the selective catalytic oxidation of CO to CO2 at
ambient temperatures, can play a significant role in
increasing the fuel cell system’s CO ...
Looking by grazing incidence small angle x-ray scattering at gold nanoparticles supported on rutile TiO2(110) during CO oxidation
gold nanoparticles rutile TiO2(110)
2009/7/28
The catalytic activity of oxide-supported gold
nanoparticles depends crucially on their size. The
present work describes a dedicated set-up in which
particle size is determined by grazing incidence...